Effects of Annealing Temperature and Epoxy Resin Encapsulation on Soft Magnetic Properties of Fe78Si9B13 Amorphous Alloy
-
摘要: 采用单辊法制备了宽20 mm、厚25 μm的Fe78Si9B13非晶带材, 再将其绕制成环形磁芯, 然后在350, 400, 450, 500 ℃下对环形磁芯进行退火处理; 采用环氧树脂对400 ℃退火的磁芯进行封装, 研究了退火温度和环氧树脂封装对Fe78Si9B13非晶合金软磁性能的影响。结果表明: 随着退火温度升高, Fe78Si9B13非晶合金的初始磁导率μi、饱和磁感应强度Bs和矫顽力Hc均呈先增大后减小的趋势; 当退火温度为400 ℃时, Fe78Si9B13非晶合金的综合软磁性能最佳, μi为0.008 3 H·m-1, Bs为1.517 T, Hc为15.73 A·m-1; 采用环氧树脂封装后, Fe78Si9B13非晶合金的μi和Bs减小,Hc增大, 它的磁化曲线和磁滞回线与封装前的基本重合。
-
关键词:
- Fe78Si9B13非晶合金 /
- 退火 /
- 环氧树脂封装 /
- 软磁性能
Abstract: Fe78Si9B13 amorphous strips with 20 mm width and 25 μm thickness were prepared by single-roller method. Magnetic cores were gained by coiling the amorphous strips, and then were annealed at 350, 400, 450, 500 ℃, respectively. Magnetic core annealed at 400 ℃ was encapsulated using epoxy resin, and the effects of annealing temperature and epoxy resin encapsulation on the soft magnetic properties were studied. The results show that the initial magnetic permeability (μi), saturation magnetization (Bs) and coercivity (Hc) all increased at first and then decrease with the increase of annealing temperature. The comprehensive soft magnetic properties of Fe78Si9B13 amorphous alloy annealed at 400 ℃ show the best (μi=0.008 3 H·m-1, Bs=1.517 T and Hc=15.73 A·m-1. The μi and Bs of Fe78Si9B13 amorphous alloy all decreased and its Hc increased after epoxy resin encapsulation. The magnetizaion curve and hysteresis hoop of Fe78Si9B13 amorphous alloy after encapsulation were mainly the same with those before encapsulation. -
-
[1] KLEMENT W, WILLENS R H, DUWEZ P. Non-crystalline structure in solidified gold-silicon alloys［J］. Nature, 1960,31: 869-870. [2] HASEGAWA R. Applications of amorphous magnetic alloys in electronic devices［J］.Journal of Non-crystalline Solids,2001,287: 405-412. [3] MALKINSKI L M.The role of residual stresses in magnetostrictive metallic glasses ［J］.J Magn Magn Mater,1995,140/144: 267-268. [4] 朱正吼, 宋晖, 严明明, 等.FeCuNbSiB非晶软磁带材的制备及其缺陷分析［J］.机械工程材料, 2004,28(10): 48-50. [5] 夏小鸽, 朱正吼, 马广斌, 等.基于磁芯的环氧树脂基封装材料研究［J］.功能材料, 2008,39(1): 36-40. [6] 黄伟兵, 朱正吼, 杨操兵, 等.Fe/FeSiB磁粉芯软磁性能研究［J］.功能材料, 2010,41(11): 2010-2013. [7] 宛德福, 罗世华.磁性物理［M］.北京: 电子工业出版社, 1987: 236. [8] 姜敏凤, 陈文智.退火态Fe-S-iB非晶合金恒导磁性能研究［J］.金属热处理, 2010,35(12): 116-118. [9] 尹镭, 朱正吼, 郑海娟, 等.Fe78Si9B13非晶合金磁芯封装及其软磁性能［J］.功能材料, 2012,43(6): 722-724. [10] 蒋达国, 黄坚革.Fe78Si9B13非晶薄带的巨磁阻抗效应［J］.机械工程材料, 2011,35(1): 43-45. [11] 沈桂娣, 李建平, 周传伟.铁基非晶软磁合金及其晶化［J］. 南京理工大学学报,1998,22(6): 544-547. [12] 夏小鸽, 朱正吼, 马广斌.基于磁芯的环氧树脂基封装材料研究［J］.功能材料, 2008,39(1): 36-40. [13] 唐妹红, 叶周军, 李荣云.非晶态带材表面处理研究［C］//第十五届全国复合材料学术会议论文集(上册).北京: 国防工业出版社, 2008: 620-622.
计量
- 文章访问数: 3
- HTML全文浏览量: 0
- PDF下载量: 0
下载: