Abstract: 102/T91 dissimilar steel tubes were joined by transient liquid-phase (TLP) bonding process of two-step heating temperature using FeNiCrSiB amorphous alloy as filler in argon atmosphere.Microstructure and mechanical properties of the joint was tested at room temperature.The results showed that 102/T91 joint with similar compositions to the parent metal,curved interface and higher tensile strength than the base metal could be gained under following conditions of heating at 1 260 ℃ for 1 min,freezing at 1 230 ℃ for 4 min with the pressure of 6 MPa.