孔结构参数对通孔多孔铝合金超声衰减性能的影响
Effect of Porous Structural Parameters on Ultrasonic Attenuation Capacity of Porous Al Alloy with High Specific Strength
-
摘要: 研究了通孔多孔铝合金的超声衰减性能.结果表明:通孔多孔铝合金在1~10MHz范围内是一种具有良好超声衰减性能的轻质材料,超声衰减系数α随孔径d的减小、孔隙率Ps减小和比表面积Sv的增加而增大.Abstract: Ultrasonic attenuation capacity of porous Al alloy with high specific strength was studied.That alloy is a light material with good ultrasonic attenuation capacity between 1-10MHz.Ultrasonic attenuation coefficient α of porous Al alloy increases with decreasing pore diameter d,with decreasing porosity Ps and with increasing specific surface Sv.