铸态与轧制态纯铝等径角挤压变形后的组织与性能

基金项目:

国家自然科学基金资助项目(59971015)

详细信息

Microstructure and Mechanical Properties of Cast and Rolled Pure Al Deformed by Equal Channel Angular Pressing

摘要: 对铸态及轧制态的纯铝进行了等径角挤压(ECAP) 变形,用透射电镜观察了变形后的显微组织,并对不同道次变形后的材料进行了硬度测定.结果表明:ECAP方法可使纯铝组织获得显著细化,在相同的变形条件下,铸态与轧制态纯铝均获得了等轴细晶组织,且晶粒尺寸相差不大.1道次ECAP变形后材料的硬度明显增大,随后每道次硬度的增大趋势明显变缓.这说明初始状态对ECAP变形后的组织和性能影响不大.
- 纯铝 /
- 等径角挤压 /
- 铸态 /
- 轧制态
Abstract: Cast and rolled Al were deformed by equal channel angular pressing (ECAP).Microstructure before and after ECAP were observed and hardness of the materials were measured.The grains in the materials could be remarkably refined by ECAP and there is no obvious difference between the deformed microstructure of specimens which had different initial states.The Vickers hardness of the materials increased after 1st pass during ECAP process and the increasing trend become slower in the following passes.The initial states have no obvious impact on the microstructure and mechanical properties of the materials during ECAP process.
- pure Al /
- equal channel angular pressing /
- cast /
- roll

[1]	Valiev R Z,Islamgaliev R K,Alexandron I V.Bulk nanostructured materials from severe plastic deformation[J].Progress in Materials Science,2000,45:103-189.
[2]	Iwahash Y,Horita Z,Nemoto M,et al.The process of grain refinement in equal-channel angular pressing[J].Acta Mater,1998,46(9):3317-3331.
[3]	程永奇,陈振华,夏伟军.镁合金等径角挤压的研究与发展[J].机械工程材料,2005,29(9):1-4.
[4]	吴世丁,李强,姜传斌,等.铜单晶ECAE过程的剪切特征[J].金属学报,2000,36(6):602-607.
[5]	Zhu Y T,Lowe T C.Observations and issues on mechanisms of grain refinement during ECAP process[J].Mater Sci Eng,2000,A291:46-53.
[6]	Iwahashi Y,Wang J,Horita Z,et al.Principle of equal channel angular pressing for the processing of ultrafine-grained materials[J].Scripta Mater,1996,35(2):143-146.
[7]	林肇琦.有色金属材料学[M].沈阳:东北工学院出版社,1986.
[8]	林均品,安希墉,雷廷权.铝合金动态再结晶模型[J].北京科技大学学报,1993,15(3):262-266.
[9]	周建.7075铝合金在锻造过程中显微组织的演变和工艺模拟[D].沈阳:东北大学,2003.
[10]	Gourdet S,Montheillet F.An experimental study of the recrystallization mechanism during hot deformation of aluminum[J].Mater Sci Eng,2000,A283:274-288.