超快速冷却终止温度对X80管线钢组织和性能的影响

基金项目:

国家自然科学基金资助项目(51004037)

中央高校基本科研业务费专项资金资助项目(N090307002)

详细信息

Effects of Ultra Fast Cooling Ending Temperature on Microstructure and Mechanical Properties of X80 Pipeline Steel

摘要: 在试验轧机上对X80管线钢进行了热轧试验, 并采用超快冷结合层流冷却的冷却方式对试验钢进行了冷却, 结合组织观测, 系统研究了超快冷终止温度对力学性能的影响。结果表明: 在超快冷终止温度为670 ℃时, 组织中发现了多边形铁素体, 试验钢屈强比较低; 随着超快冷终止温度的降低, 析出物粒子逐渐增多, 尺寸逐渐细小且弥散, 试验钢的强度和低温韧性逐渐提高, 断后伸长率先升高后降低。
- 超快冷 /
- 管线钢 /
- 显微组织 /
- 力学性能
Abstract: Hot rolling test for X80 pipeline steel was carried out at experimental rolling mills. And the test steel was cooled by ultra fast cooling and laminar cooling after rolling. Combined with the microstructure observation, effects of ultra fast cooling ending temperature on mechanical properties were investigated. Results show that when the ultra fast cooling ending temperature was about 670 ℃, polygonal ferrite was found and yield ratio of test steel was lower. With the decreasing of ultra fast cooling ending temperature, the amount of precipitates increased, the size of precipitates was finer and dispersion, the strength and toughness increaseed, elongation first increased and then decreased.
- ultra fast cooling /
- pipeline steel /
- microstructure /
- mechanical property

[1]	黄志潜.X80管线钢在高压大流量输气管道上的应用与发展前景[J].焊管,2005, 25(2):5-10.
[2]	焦多田,蔡庆武,武会宾.轧后冷却制度对X80级抗大变形管线钢组织和屈强比的影响[J].金属学报,2009,45(9):1111-1116.
[3]	钱百年,国旭明,李晶丽, 等.高强度管线钢X80的焊接研究[J].焊接,2002(8):14-17.
[4]	YANG J R, HUANG C Y, CHIOU C S. The influnce of plastic deformation and cooling rates on the microstructure constituents of an utra-low carbon bainitic steel[J].ISIJ International,1995,35(8):1013-1019.
[5]	焦百泉. 管线钢性能的发展[J].焊管,1999,22(4):1-7.
[6]	孔君华,郭斌,刘昌明,等.高钢级管线钢X80的研制与发展[J].材料导报,2004,18(4):23-25.
[7]	薛小怀,杨淑芳,吴鲁海,等.X80管线钢的研究进展[J].上海金属,2004,26(2):45-47.
[8]	王国栋.以超快冷为核心的新一代TMCP技术[J].上海金属,2008,30(2):1-5.
[9]	AURELIE L, PIERRE S, GUILLAUME B, et al. Metallurgical aspects of ultra fast cooling in front of the down-coiler[J].Steel Research Int,2004,75(2):139-146.
[10]	HERMAN J C. Impact of new rolling and cooling technologies on thermomechanically processed steels[J].Ironmaking and Steelmaking,2001,28(2):159-163.