    冷轧钢板表面缺陷的种类及形成原因

    Types and Forming Reasons of Cold Rolled Steel Plate Surface Defects

      摘要
    • 摘要: 对冷轧钢板生产中出现的表面缺陷进行了分类, 主要分析了孔洞类、氧化铁皮压入类、边裂类、起皮类等缺陷的主要待征及产生的原因; 明确了相关缺陷产生的影响因素, 并提出了相应的预防措施。

       

      Abstract: Cold-rolled steel plate surface defects appeared during production were categorized, and the major characteristics and forming causes of holes, iron oxide press-in, edge cracking, peeling defects were mainly analyzed. The effect factors for forming defects were affirmed and some relevant preventive measures were proposed.

       