新型高锰合金钢的研制

详细信息

Development of a High Manganese Alloyed Steel

摘要: 在ZGMn13钢的基础上,通过调整成分,加入适量的合金元素铬、钼,得到新型高锰合金钢,经沉淀强化热处理后对其组织和性能进行了分析.结果表明：成分为1.2%～1.28% C,11%～13%Mn,≤0.02%S,≤0.04%P,≤0.65%Si,1.5%～1.8%Cr,0.40%～0.50%Mo的合金钢,经沉淀强化热处理后,其奥氏体晶粒细化,碳化物弥散析出,其耐磨性和加工硬化能力提高;力学性能达到σb=766 MPa,σs=458 MPa,δ=27.245%,ak=218 J/cm2, 硬度217 HBS.
- 高锰钢 /
- 合金元素 /
- 沉淀强化 /
- 奥氏体
Abstract: A new high manganese alloy steel has been obtained by adjusting chemical composition and addition of alloying elements in ZGMn13 steel.The structure and properties of the high manganese alloy steel after precipitation hardening heat treatment were analyzed.The high manganese alloy steel containing 1.2%-1.28%C,11%-13%Mn,≤0.02% S,≤0.04%P,≤0.65%Si,1.5%-1.8%Cr and 0.40%-0.50% Mo after suitable precipitation hardening treatment could make austenitic transforming completely and refine austenitic grain,and get dispersed pellet-like carbides.The wear resistance of the steel increased via working hardening and fine dispersion of the second phase.The mechanical properties of the alloy steel could achieve σb=766 MPa,σs=458 MPa,δ=27245%,ak=218 J/cm2 and hardness 217 HBS.
- high manganese steel /
- alloying element /
- precipitation hardening /
- austenite

[1]	谢敬佩,李卫,宋延沛,等.耐磨铸钢及熔炼[M].北京:机械工业出版社,2003.
[2]	马广清,于文馨,符莉,等.水韧处理工艺对合金高锰钢组织和性能的影响[J].铸造,2004,(4):308-309.
[3]	陈希杰.高锰钢[M].北京:机械工业出版社,1989.
[4]	何力,金志浩,卢锦德.合金化奥氏体锰钢的研究[J].机械工程材料,2000,24(2):22-24.
[5]	李树索,陈希杰.高锰钢的发展与应用[J].矿山机械,1998,(3):70-71.
[6]	张增志.耐磨高锰钢[M].北京:冶金工业出版社,2002.
[7]	丛勉.铸造手册.第二卷.铸钢[M].北京:机械工业出版社,2002.