Accelerated Aging Behavior of Nitrile-Butadiene Rubber in Hydraulic Oil

YU Jin-tao; WANG Zhan-bin; FAN Jin-juan; YUAN Li-hua

doi:10.11973/jxgccl201704022

Materials and Mechanical Engineering > 2017 > 41(4): 103-105,110. > DOI: 10.11973/jxgccl201704022

YU Jin-tao, WANG Zhan-bin, FAN Jin-juan, YUAN Li-hua. Accelerated Aging Behavior of Nitrile-Butadiene Rubber in Hydraulic Oil[J]. Materials and Mechanical Engineering, 2017, 41(4): 103-105,110. DOI: 10.11973/jxgccl201704022

Citation:

PDF (3657 KB)

Accelerated Aging Behavior of Nitrile-Butadiene Rubber in Hydraulic Oil

1. Key Laboratory of Nondestructive Test(Ministry of Education), Nanchang Hangkong University, Nanchang 330063, China;
2. Beijing Key Laboratory of Aeronautical Materials Testing and Evaluation, Beijing Institute of Aeronautical Materials, Beijing 100095, China

More Information

Received Date: March 18, 2016
Revised Date: March 02, 2017

Graphical Abstract

Abstract

Abstract

The high-temperature accelerated aging tests in hydraulic oil with temperatures of 110 ℃, 130 ℃ and 150 ℃ were carried out on a nitrile-butadiene rubber. Then the effects of aging time on the tensile property and hardness of the rubber were studied and the aging behavior was analyzed. The service life of the rubber was also predicted by using Arrhenius equation. The results show that during the aging process, under the combined effects of oil swelling, crosslinking and chain broking, the tensile strength of the nitrile-butadiene rubber first kept unchanged then decreased, the hardness first decreased then increased and the maximum percentage elongation decreased exponentially. According to the maximum percentage elongation data, the service life predicted by Arrhenius equation of the nitrile-butadiene rubber in 25 ℃ hydraulic oil was 2 836 d, which was equivalent to the real life. The prediction result was relatively accurate.
- nitrile-butadiene rubber,
- hydraulic oil,
- accelerated aging,
- exponential law

FullText(HTML)

References (17)

References

[1]	JOHN S D. Rubber technology: Compounding and testing for performance[M]. Munich: Carl Hanser Verlag, 2001.
[2]	张录平,李晖,刘亚平,等. 橡胶材料老化试验的研究现状及发展趋势[J]. 弹性体,2009, 19(4):60-63.
[3]	BAUER D R, BALDWIN J M, ELLWOOD K R. Rubber aging in tires. Part 2: Accelerated oven aging tests[J]. Polymer Degradation and Stability, 2007, 92(1):110-117.
[4]	HAKKARAINEN M, ALBERTSSON A C. Indicator products: A new tool for lifetime prediction of polymeric materials[J]. Biomacromolecules, 2005, 6(2):775-779.
[5]	余超,文庆珍,朱金华,等. 基于强韧度的特种氯丁橡胶使用寿命预测研究[J]. 弹性体, 2011,21(1):15-18.
[6]	李吟今. 利用时间外延法预测硫化胶常温老化应力松弛和永久变形性能的研究[J]. 橡胶工业, 2002, 49(10):615-622.
[7]	MORRELL P R, PATEL M, SKINNER A R. Accelerated thermal aging studies on nitrile rubber O-rings[J]. Polymer Testing, 2003, 22(6):651-656.
[8]	赵建峰,余超,魏徽. 基于抗拉强度的特种氯丁橡胶使用寿命预测[J]. 弹性体,2013,23 (5):15-18.
[9]	熊英,付宝强,郭少云,等. 丁腈橡胶应力加速老化行为的研究[J]. 装备与环境工程, 2012,9(3):52-56.
[10]	李咏今. 硫化胶烘箱加速老化与室内自然老化相关性的研究[J]. 特种橡胶制品, 2001,22(4):51-56.
[11]	曾德智,李坛,雷正义,等. 承压状态下氟橡胶O型密封圈耐酸性介质腐蚀性能[J]. 机械工程材料,2014, 38(8):88-92.
[12]	郑亮. 原油对丁腈橡胶密封件性能的影响[J]. 橡塑技术与装备,2012,38(3):53-57.
[13]	孙默冉. 丁腈橡胶制品及其助剂在变压器油中老化机理研究[D]. 沈阳:沈阳工业大学,2013.
[14]	张劲,孙汝楠,孟思炜,等. 炭黑/高分散白炭黑对丁腈橡胶耐热及耐油性能的影响[J]. 硅酸盐通报,2014 (12):3159-3165.
[15]	张凤玲,代想想,王越,等. 航空液压油对丁腈橡胶密封件性能的影响[J]. 中国橡胶,2013,29(5):42-46.
[16]	王占彬,肖淑华,范金娟,等. 丁腈橡胶密封圈液压油中的老化机理[J]. 宇航材料工艺,2014,44(4):64-67.
[17]	陈跃如,刘亚青,张录平,等. 硅橡胶密封材料热氧老化研究[J]. 弹性体,2011,21(5):6-9.

Cited By

Get Citation

PDF

XML

Article views (7) PDF downloads (0)

Turn off MathJax

Article Contents

Abstract

References

Accelerated Aging Behavior of Nitrile-Butadiene Rubber in Hydraulic Oil

Abstract

References

Catalog

Export File

Citation

Format

Content