Forming Limit for As-quenched 2A12 Aluminum Alloy

ZHANG Peng; CHEN Minghe; YE Jianhua

doi:10.11973/jxgccl201806011

Materials and Mechanical Engineering > 2018 > 42(6): 55-58. > DOI: 10.11973/jxgccl201806011

ZHANG Peng, CHEN Minghe, YE Jianhua. Forming Limit for As-quenched 2A12 Aluminum Alloy[J]. Materials and Mechanical Engineering, 2018, 42(6): 55-58. DOI: 10.11973/jxgccl201806011

Citation:

ZHANG Peng, CHEN Minghe, YE Jianhua. Forming Limit for As-quenched 2A12 Aluminum Alloy[J]. Materials and Mechanical Engineering, 2018, 42(6): 55-58. DOI: 10.11973/jxgccl201806011

Citation:

ZHANG Peng, CHEN Minghe, YE Jianhua. Forming Limit for As-quenched 2A12 Aluminum Alloy[J]. Materials and Mechanical Engineering, 2018, 42(6): 55-58. DOI: 10.11973/jxgccl201806011

PDF (4373 KB)

Forming Limit for As-quenched 2A12 Aluminum Alloy

College of Mechanical and Electrical Engineering, Nanjing University of Aeronautics and Astronautics, Nanjing 210016, China

More Information

Received Date: May 11, 2017
Revised Date: May 14, 2018

Graphical Abstract

Abstract

Abstract

As-quenched 2A12 aluminum alloy specimens with nine kinds of size obtained after aging at room temperature for 10, 20, 30 min, respectively, were bulged under three types of lubrication conditions including solid lubrication, liquid lubrication and no lubrication, respectively. The forming limit diagram of the aluminum alloy was obtained, and the effect of aging time on the formability was analyzed. The results show that the as-quenched 2A12 aluminum alloy obtained after aging for 10 min had good formability. With the increase of aging time, the forming limit curves moved down, indicating that the plasticity of the aluminum alloy decreased and the forming safety area became smaller. The appropriate natural aging time of 2A12 aluminum alloy before forming was within 10 min.
- 2A12 aluminum alloy,
- as-quenching,
- natural aging,
- forming limit

FullText(HTML)

References (15)

References

[1]	中国航空材料手册编委会.中国航空材料手册:第三卷[M]. 北京:中国标准出版社,2002.
[2]	飞机设计手册总编委会.飞机设计手册:第3册上[M].北京:航空工业出版社,2004.
[3]	KEELER S P, BACKOFEN W A. Plastic instability and fracture in sheets stretched over rigid punches[J]. Trans ASM Q, 1963,56(1):25-48.
[4]	GOODWIN G M. Application of strain analysis to sheet metal forming problems in the press shop[C]//1968 Automotive Engineering Congress and Exposition.[S.l.]:SAE, 1968:680093.
[5]	王辉. 成形极限图的获取方法与其在金属板料成形中的应用[D].南京:南京航空航天大学,2011.
[6]	陈明和, 高霖, 薛玉雷,等. 板料应力成形极限判据的有限元分析程序[J].南京航空航天大学学报,2005,37(增刊1):68-71.
[7]	张成祥, 陈明和, 雷晓晶, 等. GH600合金薄板成形极限研究[J]. 航空材料学报, 2015, 35(6):35-40.
[8]	张成祥, 陈明和, 雷晓晶,等. GH163合金成形极限图及应用[J]. 塑性工程学报, 2016, 23(1):93-98.
[9]	高宏志, 周贤宾. 新淬火状态铝合金板的成形极限[J]. 北京航空航天大学学报, 2006, 32(9):1083-1086.
[10]	高宏志, 周贤宾. 新淬火状态硬铝合金板的成形性能及数值模拟[J]. 航空材料学报, 2008, 28(5):27-31.
[11]	黄华, 李大永, 彭颖红. 7075-T6铝合金板温热成形极限图实验[J]. 塑性工程学报, 2010, 17(1):93-97.
[12]	陈劫实, 周贤宾. 板料成形极限预测新判据[J]. 机械工程学报, 2009, 45(4):64-69.
[13]	DOEGE E, DRÖDER K. Sheet metal forming of magnesium wrought alloys:Formability and process technology[J]. Journal of Materials Processing Technology, 2001, 115(1):14-19.
[14]	LI D M, GHOSH A. Tensile deformation behavior of aluminum alloys at warm forming temperatures[J]. Materials Science and Engineering:A, 2003, 352(1/2):279-286.
[15]	陈新平, 汪承璞. 一种预测左半部成形极限图的简单方法[J]. 金属成形工程, 2000, 18(4):4-6.

Cited By

Get Citation

PDF

XML

Article views (3) PDF downloads (2)

Turn off MathJax

Article Contents

Abstract

References

Forming Limit for As-quenched 2A12 Aluminum Alloy

Abstract

References

Catalog

Export File

Citation

Format

Content