LIU Jixiong, WANG Wenjun, HUANG Tuo, WANG Xin, WANG Xiaoxiang, WANG Dingchun, GAO Qi. Effect of Diffusion Bonding Process on Connection Interface Bonding Propertyof SP-700 Titanium Alloy Hot Rolled Sheet[J]. Materials and Mechanical Engineering, 2020, 44(8): 23-26. DOI: 10.11973/jxgccl202008005
Citation: LIU Jixiong, WANG Wenjun, HUANG Tuo, WANG Xin, WANG Xiaoxiang, WANG Dingchun, GAO Qi. Effect of Diffusion Bonding Process on Connection Interface Bonding Propertyof SP-700 Titanium Alloy Hot Rolled Sheet[J]. Materials and Mechanical Engineering, 2020, 44(8): 23-26. DOI: 10.11973/jxgccl202008005

Effect of Diffusion Bonding Process on Connection Interface Bonding Propertyof SP-700 Titanium Alloy Hot Rolled Sheet

More Information
  • Received Date: November 25, 2019
  • Revised Date: June 18, 2020
  • Diffusion bonding test was performed on SP-700 titanium alloy hot rolled sheet, and the effects of diffusion bonding temperature (720, 750, 780, 810, 840 ℃) and time (5, 15, 30, 45 min) on the connection interface morphology and bonding strength were studied. The results show that with the increase of diffusion bonding temperature and time, the unbonded area of the alloy decreased until disappeared, and the interface bonding strength increased. The higher the temperature, the shorter the time interval required for fully integrating of the interface. When the bonding temperature was higher than 750 ℃ and time was 30 min, the interface was basically fully integrated. After diffusion bonding at 840 ℃ for 30 min, many equiaxed α phases existed on the bonding interface, and the interface bonding strength was the highest, reaching 400 MPa.
  • [1]
    黄金昌. SP700钛合金的开发和应用[J]. 稀有金属与硬质合金, 1998, 134(9): 58-62.
    [2]
    王悔改,李文博,李鑫鑫,等.SP700钛合金的多重固溶时效处理[J].铸造技术,2014,35(9):1990-1993.
    [3]
    陈梦薇,李淼泉.固态扩散连接空洞闭合模型的研究进展[J].材料导报,2010,24(9):101-104.
    [4]
    徐子文, 阮中健, 张桂林, 等. 扩散连接中界面迁移机制研究[J]. 焊接技术, 2003, 32(1): 8-9.
    [5]
    林兆荣,张中元.超塑性状态下Ti-6Al-4V钛合金扩散连接研究[J].航空学报,1992,13(5):288-295.
    [6]
    TSAY L W,DING Y S,CHUNG W C,et al.Notched tensile strength of SP-700 laser welds[J].Materials Letters, 2008,62(6/7):1114-1117.
    [7]
    TSAY L W,HSU C L,CHEN C.Notched tensile fracture of Ti-4.5Al-3V-2Fe-2Mo welds at elevated temperatures[J].Materials Chemistry and Physics, 2010,120(2/3):715-721.
    [8]
    GUNAWARMA N,NINOMI M,EYLON D,et al.Improvement in fracture toughness of Ti-4.5Al-3V-2Mo-2Fe through microstructural optimization[J].Metallurgical and Materials Transactions A, 2003,34(2):267-275.
    [9]
    CHU C Y,HSIEH C T,TSAY L W.Microstructure and notched tensile fracture of Ti-6Al-4V to Ti-4.5Al-3V-2Fe-2Mo dissimilar welds[J].Materials & Design, 2014,63:14-19.
    [10]
    徐子文, 阮中健, 张桂林, 等. 扩散连接中界面迁移机制研究[J]. 焊接技术, 2003,32(1): 8-9.

Catalog

    Article views (3) PDF downloads (0) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return