ZHANG Xinning, ZHANG Yingying. Microscopic Failure Mechanism of Graphite in Ferrite Ductile Iron[J]. Materials and Mechanical Engineering, 2021, 45(11): 24-28. DOI: 10.11973/jxgccl202111005
Citation: ZHANG Xinning, ZHANG Yingying. Microscopic Failure Mechanism of Graphite in Ferrite Ductile Iron[J]. Materials and Mechanical Engineering, 2021, 45(11): 24-28. DOI: 10.11973/jxgccl202111005
shu

Microscopic Failure Mechanism of Graphite in Ferrite Ductile Iron

  • School of Mechanical Engineering, Liaoning Petrochemical University, Fushun 113001, China

More Information
  • Received Date: November 01, 2020
  • Revised Date: October 11, 2021
    Graphical Abstract
    • Abstract
  • The failure mechanism of graphite in ferrite ductile iron under tensile and impact action was studied by in-situ microscopic observation. The influence of morphology and distribution of graphite nodules on the micro-mechanism of crack initiation and propagation was analyzed. The results show that the graphite nodules separated from the matrix when the graphite nodules uniformly distributed and the spacing was larger than the average graphite size under tensile action, and there were radial cracks in the graphite nodule or cracks throughout the whole graphite. When graphite nodules showed aggregative distribution and spacing was smaller than the average size of graphite, the cracks between the graphite nodules and the matrix connected to form larger cracks. Under impact loads, there were complementary failure mechanisms such as "onion-like" cracking and internal radial cracking in graphite nodules. Lamellar tearing was observed in irregular graphite nodules under tensile and impact loads. The rapidly closed austenite shell could keep the graphite nodule rounded and the surrounding ferrite grains evenly distributed; slow closed austenite shell resulted in graphite distortion and uneven distribution of ferrite grains.
    • FullText(HTML)
    • References (15)
  • [1]
    PUSTAL B, BVHRIG-POLACZEK A.Physico-chemical causes of the formation of chunky graphite in austenitic ductile iron[J]. Acta Materialia, 2017, 124:137-142.
    [2]
    SOI AN'G SKI M.The influence of small amounts of aluminium on the spheroidization of cast iron with cerium mischmetal[J]. Archives of Foundry Engineering, 2012, 12(2):117-122.
    [3]
    KOCATEPE K, CERAH M, ERDOGAN M.The tensile fracture behaviour of intercritically annealed and quenched + tempered ferritic ductile iron with dual matrix structure[J]. Materials & Design, 2007, 28(1):172-181.
    [4]
    TOKTAŞG, TAYANÇ M, TOKTAŞA.Effect of matrix structure on the impact properties of an alloyed ductile iron[J]. Materials Characterization, 2006, 57(4/5):290-299.
    [5]
    QING J J, RICHARDS V L, AKEN D C.Examination of spheroidal graphite growth and austenite solidification in ductile iron[J]. Metallurgical and Materials Transactions A, 2016, 47(12):6197-6213.
    [6]
    FERNANDINO D O, TENAGLIA N, DI COCCO V, et al. Relation between microstructural heterogeneities and damage mechanisms of a ferritic spheroidal graphite cast iron during tensile loading[J]. Fatigue & Fracture of Engineering Materials & Structures, 2020, 43(6):1262-1273.
    [7]
    周继扬.球状石墨的形核与孕育——球墨铸铁基础理论的最新发展(一)[J]. 现代铸铁, 2002, 22(3):7-12.

    ZHOU J Y.Nucleation of spheroidal graphite and inoculation-recent development of the basic theory of spheroidal graphite cast iron(I)[J]. Modern Cast Iron, 2002, 22(3):7-12.
    [8]
    COLLINI L, PIRONDI A.Micromechanical modeling of the effect of stress triaxiality on the strain to failure of ductile cast iron[J]. Engineering Fracture Mechanics, 2020, 238:107270.
    [9]
    WARMUZEK M, POLKOWSKA A.Micromechanism of damage of the graphite spheroid in the nodular cast iron during static tensile test[J]. Journal of Manufacturing and Materials Processing, 2020, 4(1):22.
    [10]
    SHIMOKAWA T, TANAKA M, HIGASHIDA K.Effect of grain boundaries on fracture toughness in ultrafine-grained metals by atomic-scale computational experiments[J]. Materials Science Forum, 2012, 706/707/708/709:1841-1846.
    [11]
    陈江, 黄兴民, 高杰维, 等.低镍球墨铸铁低温冲击性能及断裂机理研究[J]. 材料工程, 2012, 40(12):33-38.

    CHEN J, HUANG X M, GAO J W, et al. Impact behavior and fracture mechanism of ductile cast iron with minor nickel addition at low temperature[J]. Journal of Materials Engineering, 2012, 40(12):33-38.
    [12]
    QING J, RICHARDS V L, VAN AKEN D C.Growth stages and hexagonal-rhombohedral structural arrangements in spheroidal graphite observed in ductile iron[J]. Carbon, 2017, 116:456-469.
    [13]
    LIU J H, YAN J S, ZHAO X B, et al. Precipitation and evolution of nodular graphite during solidification process of ductile iron[J]. China Foundry, 2020, 17(4):260-271.
    [14]
    张晛韦, 张红伟, 雷洪, 等.球墨铸铁离异共晶凝固组织生长模拟[J]. 钢铁研究学报, 2020, 32(9):816-825.

    ZHANG X W, ZHANG H W, LEI H, et al. Simulation of divorced eutectic microstructure evolution in ductile iron solidification process[J]. Journal of Iron and Steel Research, 2020, 32(9):816-825.
    [15]
    周继扬.石墨的球状生长——球墨铸铁基础理论的最新发展(二)[J]. 现代铸铁, 2002, 22(4):1-6.

    ZHOU J Y.Spheroidal growth of graphite-Latest development of the basic theory of spheroidal graphite cast iron(Part II)[J]. Modern Cast Iron, 2002, 22(4):1-6.
    • Related Articles

Catalog

    Get Citation
    PDF
    XML
    Article views (9) PDF downloads (2) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    References

    Materials and Mechanical Engineering

    Address：99 Handan Road, ShanghaiPost Code: 200437

    Tel：021-65556775-368Email:mem@mat-test.com

    沪ICP备17055736号-5

    Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return