LUO Xiao-yan, LIU Gui-zhong, GAO Yuan. Hardness and Electrochemical Property of As Annealed Multi-Component AlFeCoNiCrTiV0.5 High-Entropy Alloy[J]. Materials and Mechanical Engineering, 2011, 35(4): 87-90.
Citation: LUO Xiao-yan, LIU Gui-zhong, GAO Yuan. Hardness and Electrochemical Property of As Annealed Multi-Component AlFeCoNiCrTiV0.5 High-Entropy Alloy[J]. Materials and Mechanical Engineering, 2011, 35(4): 87-90.

Hardness and Electrochemical Property of As Annealed Multi-Component AlFeCoNiCrTiV0.5 High-Entropy Alloy

More Information
  • Received Date: February 13, 2011
  • The annealed microstructure, hardness and electrochemical property of the AlFeCoNiCrTiV0.5 high-entropy alloy were studied by using XRD, SEM, DSC and Rockwell apparatus, etc., The results show that the peak position of bcc1 and bcc2 phases approached gradually with the increase of annealing temperature. Diffraction peaks of the two phases coincided at lower angle when the annealing temperature reached 900 ℃. The bcc1 phase transformed to fcc phase when the temperature reached 1 100 ℃. The hardness of the alloy kept 52.3 HRC when the annealing temperature was up to 1 100 ℃ and the alloy exhibited superior resistance to tempering and softening property. The alloy had lower corrosion rate than 304 stainless steel in 0.5 mol·L-1 H2SO4 solution. The corrosion rate of the alloy was similar with 304 stainless steel in 1 mol·L-1 NaCl solution, but their corrosion resistance property was better than 304 stainless steel.
  • [1]
    TONG C J, CHEN S K, YEH J W,et al. Microstructure characterization of AlxCoCrCuFeNi high-entropy alloy system with multi-principal elements[J].Metall Mat Trans A,2005,36:881-893.
    [2]
    陈敏, 刘源, 李言祥,等.多主元高熵合金AlTiFeNiCuCrx微观结构和力学性能[J].金属学报, 2007, 43(10): 1020-1024.
    [3]
    刘源, 李言祥, 陈祥,等.多主元高熵合金研究进展[J].材料导报, 2006, 20(4):4-6.
    [4]
    刘源, 陈敏, 李言祥.多主元高熵合金的组织和性能特点[J].特种铸造及有色合金, 2006(增刊): 252-255.
    [5]
    李伟, 刘贵仲, 郭景杰.AlxFeCoNiCrTi系高熵合金的组织结构及电化学性能研究[J].铸造, 2009, 58(5): 431-435.
    [6]
    童重缙.Cu-Co-Ni-Cr-Al-Fe高熵合金变形结构与高温特性之研究[D].台湾:台湾清华大学, 2002.
    [7]
    陈岳锋.CoCrFrNiTi高乱度合金块材与薄膜性质之研究[D].台湾:台湾私立中国文化大学, 2004.

Catalog

    Article views (7) PDF downloads (0) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return