ZHANG Ya-jun, GAO Ling-qing, ZHANG Li-juan. Propagation Characteristics of Low Cycle Fatigue Surface Crack of 10CrNiMo Structural Steel during Cantilever Bend Loading Process[J]. Materials and Mechanical Engineering, 2012, 36(6): 9-12.
Citation: ZHANG Ya-jun, GAO Ling-qing, ZHANG Li-juan. Propagation Characteristics of Low Cycle Fatigue Surface Crack of 10CrNiMo Structural Steel during Cantilever Bend Loading Process[J]. Materials and Mechanical Engineering, 2012, 36(6): 9-12.
shu

Propagation Characteristics of Low Cycle Fatigue Surface Crack of 10CrNiMo Structural Steel during Cantilever Bend Loading Process

More Information
  • Received Date: December 23, 2011
    Graphical Abstract
    • Abstract
  • The strain of surface crack front of cantilever bend loaded sample was controlled by COD displacement gage, the propagation characteristics of low cycle fatigue surface crack of 10CrNiMo structural steel were studied by increasing the strain gradually, and the fracture morphology was observed by scanning electron microscopy. The results show that the surface crack propagation rate had good power ruler relation with the total strain range for crack front. Some tyre-figure appeared near the crack source, serious squeezing happened at the beginning stage of crack propagation, major secondary cracks were found at the middle stage of crack propagation, the fatigue striation was obvious at the late stage of crack propagation, and typical dimples were found on the last fracture area.The crack propagated in sharpening-blunting mechanism and fractured in toughness mode finally.
    • FullText(HTML)
    • References (8)
  • [1]
    段权, 程光旭, 姜培正. 16MnR低周疲劳裂纹萌生寿命的统计分布研究[J].材料工程, 2000, 17(1): 42-46.
    [2]
    陈泳, 张京海, 李晓泉.800 MPa级别钢熔敷金属热处理脆化机理研究[J].材料开发与应用, 2008, 23(6): 33-37.
    [3]
    陈传尧.疲劳与断裂[M].武汉: 华中科技大学出版社, 2002.
    [4]
    NEWMAN J C, RAJU I S. An empirical stress-intensity factor equation for the surface crack[J].Engineering Fracture Mechanics, 1981, 15(1/2): 185-192.
    [5]
    舰船材料编辑室.大型焊接结构用材料的低周疲劳裂纹扩展抗力[C]//断裂力学在造船工程上的应用.[S.l.]: [s.n], 1975: 100-121.
    [6]
    张亚军, 梁健, 张欣耀, 等.一种悬臂弯曲加载表面裂纹扩展试样及其应用[J].中国测试, 2009, 35(1): 94-96.
    [7]
    石德珂, 金志浩.材料力学性能[M].西安: 西安交通大学出版社, 2008.
    [8]
    张栋, 钟培道, 陶春虎.机械失效的实用分析[M].北京: 国防工业出版社, 1997.
    • Related Articles

Catalog

    Get Citation
    PDF
    XML
    Article views (2) PDF downloads (0) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    References

    Materials and Mechanical Engineering

    Address：99 Handan Road, ShanghaiPost Code: 200437

    Tel：021-65556775-368Email:mem@mat-test.com

    沪ICP备17055736号-5

    Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return