Reason of 20SiMn<sub>2</sub>MoVA Steel with Low Impact Property

ZHANG Zhong-qi; YU Zhi-gang; LI Guang-xin; MA Xin-pei

ZHANG Zhong-qi, YU Zhi-gang, LI Guang-xin, MA Xin-pei. Reason of 20SiMn2MoVA Steel with Low Impact Property[J]. Materials and Mechanical Engineering, 2010, 34(7): 77-79.

Citation:

ZHANG Zhong-qi, YU Zhi-gang, LI Guang-xin, MA Xin-pei. Reason of 20SiMn2MoVA Steel with Low Impact Property[J]. Materials and Mechanical Engineering, 2010, 34(7): 77-79.

Citation:

ZHANG Zhong-qi, YU Zhi-gang, LI Guang-xin, MA Xin-pei. Reason of 20SiMn2MoVA Steel with Low Impact Property[J]. Materials and Mechanical Engineering, 2010, 34(7): 77-79.

Reason of 20SiMn₂MoVA Steel with Low Impact Property

Abstract

Abstract

The reason why the 20SiMn2MoVA steel with low impact toughness was analyzed by using OM,SEM,TEM and EPMA.The improvement was pointed out.The results show that chemical composition had element spot segregation,non martensite microstructure generated and carbide precipitated which resulted in low impact toughness of 20SiMn2MoVA steel after quenching and low temperature tempering.Increase the quenching temperature and cooling speed properly will benefit to decrease the amount of the non martensite and increase the impact toughness.

FullText(HTML)

References (4)

Cited By

Turn off MathJax

Article Contents

Reason of 20SiMn2MoVA Steel with Low Impact Property

Abstract

Catalog

Export File

Citation

Format

Content

Reason of 20SiMn₂MoVA Steel with Low Impact Property