LI Zhen, ZHAO Ai-min, CAO Jia-li, TANG Di. Content and Stability of Retained Austenite in High Strength Medium-Mn TRIP Steel[J]. Materials and Mechanical Engineering, 2012, 36(1): 62-64.
Citation: LI Zhen, ZHAO Ai-min, CAO Jia-li, TANG Di. Content and Stability of Retained Austenite in High Strength Medium-Mn TRIP Steel[J]. Materials and Mechanical Engineering, 2012, 36(1): 62-64.
shu

Content and Stability of Retained Austenite in High Strength Medium-Mn TRIP Steel

More Information
  • Received Date: November 30, 2011
    Graphical Abstract
    • Abstract
  • A desinged medium-Mn transformation-induced plasticity (TRIP) steel was treated by a new heat treatment, the content and stability of retained austentite were studied, the microstructure and mechanical properties of the steel were analyzed. The results show that the volum fractions of retained austenite contents in the medium-Mn TRIP steel after annealing were all over 39%, and they almost transformed into martensite during deformation process and thus increased the plasticty and stregth of the steel. The tensile strength(σb), elongation δ and σb·δ respectively were over 100 MPa, 30%, 30 GPa·%, and volume fraction of retained austenite was 51.14% after annealing at 630 ℃.
    • FullText(HTML)
    • References (6)
  • [1]
    董瀚, 王毛球, 翁宇庆.高性能钢的M3组织调控理论与技术[J].钢铁, 2010, 45(7): 1-6.
    [2]
    WAGONER R H, Advanced high-strength steel workshop[R].Arlington, USA: [s.n.], 2006: 22-23.
    [3]
    MATLOCK D K, SPEER J G. Design considerations for the next generation of advanced high strength sheet steels[C]//Proc of the 3rd Int Conf on Advanced Structural Steels (ICASS). Geongju, Korea: [S.n.],, 2006: 774-781.
    [4]
    周玉.材料分析方法[M].北京: 机械工业出版社, 2006.
    [5]
    KOH-ICHI S, JYUNYA S, TSUTOMU I, et al.Stretch-flange ability of a high-strength TRIP type bainitic sheet steel[J].ISIJ Int, 2000, 40(9): 920.
    [6]
    SPEER J, MATLOCK D K, COOMAN B C. Carbon partitioning into austenite after martensite transformation[J]. Acta Materialia, 2003, 51: 2611-2622.
    • Related Articles

Catalog

    Get Citation
    PDF
    XML
    Article views (2) PDF downloads (0) Cited by()
    Turn off MathJax
    Article Contents
    Abstract
    References

    Materials and Mechanical Engineering

    Address：99 Handan Road, ShanghaiPost Code: 200437

    Tel：021-65556775-368Email:mem@mat-test.com

    沪ICP备17055736号-5

    Supported by: Beijing Renhe Information Technology Co., Ltd.  Baidu Analytics

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return