SUN Quan, YAN Yu-xi, CHEN Jian-jun, PAN Hong-liang. Prediction for Edge Cracking for Silicon Steel Sheet with Edge Defect during Cold Rolling Based on GTN Damage Model[J]. Materials and Mechanical Engineering, 2013, 37(1): 93-97.
Citation: SUN Quan, YAN Yu-xi, CHEN Jian-jun, PAN Hong-liang. Prediction for Edge Cracking for Silicon Steel Sheet with Edge Defect during Cold Rolling Based on GTN Damage Model[J]. Materials and Mechanical Engineering, 2013, 37(1): 93-97.

Prediction for Edge Cracking for Silicon Steel Sheet with Edge Defect during Cold Rolling Based on GTN Damage Model

More Information
  • Received Date: September 21, 2012
  • The crack initiation and propagation of silicon steel strip with edge defect during cold rolling process was studied by using GTN damage model in this paper. Nine damage parameters in GTN model were identified by tensile testing and microstructure observing, and then the FE simulation of edge defect evolution of silicon steel strip during rolling process was conducted on the base of GTN damage model, and then the results were compared with rolling experimental results. The results show that the edge defect was a important reason for edge-crack initiation and propagation, and GTN damage model could be used to predict the occurrence of edge-crack of steel strip with edge defect during cold rolling process.The predicted results matched the experimental ones.
  • [1]
    NA D H, LEE Y. FE simulation of edge crack initiation and propagation of conventional grain orientation electrical steel[J].International Journal of Modern Physics B, 2008, 22(31/32): 5465-5470.
    [2]
    RAJAK S A, REDDY N V. Prediction of internal defects in plane strain rolling[J].Journal of Materials Processing Technology, 2005, 159(3): 409-417.
    [3]
    GHOSH S, LI M, GARDINER D. A computational and experimental study of cold rolling of aluminum alloys with edge cracking[J].J Manuf Sci E-T ASME, 2004, 126(1): 74-82.
    [4]
    MCVEIGH C, LIU W K. Prediction of central bursting during axisymmetric cold extrusion of a metal alloy containing particles[J].International Journal of Solids and Structures, 2006, 43(10): 3087-3105.
    [5]
    黄涛. 圆盘剪切边对边裂的影响和改进[J].冶金设备, 1988(6): 33-36.
    [6]
    TVERGAARD V N A. Analysis of the cup-cone fracture in a round tensile test bar[J].Acta Metal, 1984, 32: 157-169.
    [7]
    NEEDLEMAN A T V. An analysis of ductile rupture in notched bars[J].Journal of the Mechanics and Physics of Solids, 1984, 32: 461-490.
    [8]
    CUESTA I I, ALEGRE J M, LACALLE R. Determination of the Gurson-Tvergaard damage model parameters for simulating small punch tests[J].Fatigue & Fracture of Engineering Materials & Structures, 2010, 33(11): 703-713.
    [9]
    王国珍, 张贺全, 蒲吉斌, 等.GTN损伤模型对C-Mn钢缺口拉伸试样延性断裂的预测[J].机械强度, 2008, 30(4): 647-652.
    [10]
    FALESKOG J, GAO X S, SHIH C. Cell model for nonlinear fracture analysis-Micromechanics calibration[J].International Journal of Fracture, 1998, 89(4): 355-373.
    [11]
    ABENDROTH M, KUNA M. Determination of deformation and failure properties of ductile materials by means of the small punch test and neural networks[J].Computational Materials Science, 2003, 28(3/4): 633-644.
    [12]
    郑长卿, 周利, 张克实.金属韧性破坏的细观力学及其应用研究[M].北京: 国防工业出版社, 1995.

Catalog

    Article views (2) PDF downloads (0) Cited by()

    /

    DownLoad:  Full-Size Img  PowerPoint
    Return
    Return